熔覆材料对高速钢刀具激光熔覆断屑台裂纹及硬度的影响

摘要/Abstract

摘要： 应用激光粉末熔覆技术，在高速钢车刀的前刀面上制备出断屑台。通过切削实验，对比普通高速钢车刀和含激光熔覆断屑台车刀的断屑效果，观察激光粉末熔覆断屑台的金相组织和形貌，测试激光粉末熔覆断屑台的热膨胀系数、物相和显微硬度。研究结果表明：具有激光熔覆断屑台的高速钢车刀，在切削过程中能够减小切屑的卷曲半径，从而使切屑更容易折断，实现有效断屑。用M2/WC-12Co粉末制作激光熔覆断屑台，能够实现激光熔覆层与高速钢基体的良好冶金结合，熔覆层无熔覆裂纹缺陷，熔覆层的硬度与高速钢车刀基体相近。M2/WC-12Co激光熔覆粉末适于制作高速钢刀具的激光熔覆断屑台。

关键词: 激光熔覆, 刀具, 断屑, 裂纹, 熔覆粉末

Abstract: Laser powder cladding technology was applied to fabricate laser cladding chip breakers on the rake faces of high speed steel(HSS) cutting tools. Through the cutting experiments, the chip breaking performances of common HSS cutting tools and cutting tools with laser cladding chip breakers were compared. The microstructures and morphologies of the laser cladding chip breakers were observed. Thermal expansion coefficient, phase composition and microhardness of laser cladding layers were measured. The experimental results show that HSS cutting tool with laser cladding chip breakers may reduce the curling radius of chips to break the chip more easily and realize an effective chip breaking during cutting processes. The laser cladding chip breakers made from M2/WC-12Co powder has metallurgical combined with HSS tool substrates. The laser cladding layers have no cracks and the hardness is similar to the substrates of HSS cutting tools. The M2/WC-12Co power is suitable for fabricating laser cladding chip breakers of HSS cutting tools.

Key words: laser cladding, cutting tool, chip breaking, crack, cladding powder

中图分类号:

TG42

吴毛朝；于爱兵；魏金龙；陈秋洁；孙磊；袁建东. 熔覆材料对高速钢刀具激光熔覆断屑台裂纹及硬度的影响[J]. 中国机械工程.

WU Maochao；YU Aibing；WEI Jinlong；CHEN Qiujie；SUN Lei；YUAN Jiandong. Influences of Cladding Materials on Cracks and Hardnesses of Laser Cladding Chip Breakers on High Speed Steel Cutting Tools[J]. China Mechanical Engineering.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: http://www.cmemo.org.cn/CN/

http://www.cmemo.org.cn/CN/Y2019/V30/I13/1607

参考文献

[1]SINGH T, SINGH P, DUREJA J S, et al. A Review of Near Dry Machining/Minimum Quantity Lubrication Machining of Difficult to Machine Alloys[J]. International Journal of Machining & Machinability of Materials, 2016,18(3): 213.
[2]JAWAHIR I S. Chip-forms, Chip Breakability and Chip Control [M]. Heidelberg: Springer, 2014: 178-194.
[3]SHAMOTO E, AOKI T, SENCER B, et al. Control of Chip Flow with Guide Grooves for Continuous Chip Disposal and Chip-pulling Turning[J]. CIRP Annals—Manufacturing Technology, 2011, 60(1): 125-128.
[4]何耿煌, 吴冲浒, 刘献礼, 等. 可转位刀片断屑槽断屑性能及其槽构技术研究[J]. 哈尔滨理工大学学报, 2015, 20(3):13-18.
HE Genghuang, WU Chonghu, LIU Xianli, et al. Research on the Chip-breaking Performance of Chip Breaker of Cemented Carbide Indexable Insert and Its Groove Structure Technology[J]. Journal of Harbin University of Science and Technology, 2015, 20(3):13-18.
[5]LOTFI M, FARID A A, SOLEIMANIMEHR H. The Effect of Chip Breaker Geometry on Chip Shape, Bending Moment, and Cutting Force: FE Analysis and Experimental Study[J]. International Journal of Advanced Manufacturing Technology, 2015, 78(5/8):917-925.
[6]LIAO T, JIANG F, GUO B, et al. Optimization and Influence of the Geometrical Parameters of Chip Breaker for Finishing Machining of Fe-Cr-Ni Stainless Steel[J]. International Journal of Advanced Manufacturing Technology, 2017, 93(9/12):1-13.
[7]SAHU S K, OZDOGANLAR O B. Effect of Groove-type Chip Breakers on Twist Drill Performance[J]. International Journal of Machine Tools & Manufacture, 2003, 43(6):617-627.
[8]NAKAYAMA K. A Study on Chip Breaker[J]. Bulletin of JSME, 2008, 5(17):142-150.
[9]SONG J L, LI Y T, DENG Q L, et al. Crackingmechanism of Laser Cladding Rapid Manufacturing 316L Stainless Steel[J]. Key Engineering Materials, 2010, 419/420:413-416.
[10]祝柏林, 胡木林, 陈俐, 等. 激光熔覆层开裂问题的研究现状[J]. 金属热处理, 2000(7):1-4.
ZHU Bailin, HU Mulin, CHEN Li,et al. Research Status of Cracking in Laser Cladding Layer[J]. Heat Treatment of Metals, 2000(7):1-4.
[11]FU F, ZHANG Y, CHANG G, et al. Analysis on the Physical Mechanism of Laser Cladding Crack and Its Influence Factors[J]. Optik—International Journal for Light and Electron Optics, 2012, 127(1):200-202.
[12]李闯, 刘洪喜, 张晓伟, 等. 40Cr刀具钢表面激光熔覆钴基碳化物复合涂层的组织与性能[J]. 中国激光, 2015,42(11):1103002.
LI Chuang, LIU Hongxi, ZHANG Xiaowei, et al. Microstructure and Property of Co-based Carbide Composite Coating Fabricated by Laser Cladding on 40Cr Tool Steel Surface[J]. Chinese J. Laser, 2015,42(11):1103002.
[13]杨文超, 晁明举, 孙艳敏, 等. 原位生成WB-CrB增强镍基激光熔覆层[J]. 激光与光电子学进展, 2010, 47(8):80-85.
YANG Wenchao, CHAO Mingju, SUN Yanmin, et al. In-Situ Synthesis of WB-CrB Reinforced Ni-based Coatings by Laser Cladding[J]. Laser & Optoelectronics Progress, 2010, 47(8):80-85.
[14]苗国策. 等离子喷焊Ni基WC增强耐磨涂层的研究[D].哈尔滨：哈尔滨工业大学, 2013.
MIAO Guoce. Study on Plasma Spray Welding of Ni-based WC Enhanced Wear-resistance Coating[D]. Harbin: Harbin Institute of Technology, 2013.
[15]钟敏霖, 刘文今. Stellit和NiCrSiB合金激光送粉熔覆裂纹倾向的比较研究[J]. 中国激光, 2002, 29(11):1031-1036.
ZHONG Minlin, LIU Wenjin. Comparative Research on Cracking Tendency in Powder Feeding Laser Cladding Stellite and NiCrSiB Alloys[J]. Chinese J. Laser, 2002,29(11):1031-1036.
[16]钟敏霖, 刘文今, 任家烈. NiCrSiB合金高功率激光送粉熔覆裂纹形成的敏感因素[J]. 应用激光, 2000,20(5):193-197.
ZHONG Minlin, LIU Wenjin, REN Jialie. The Critical Influence Factors on Crack Formation during High Power CO2 Laser Cladding of NiCrSiB Alloy by Powder Feeding[J]. Applied Laser, 2000,20(5):193-197.
[17]魏金龙. 高速钢车刀激光熔覆断屑台制备方法的研究[D].宁波：宁波大学, 2017.
WEI Jinlong. Study on the Preparation Method of Laser Cladding Chip Breaker of High Speed Steel Turning Tool[D].Ningbo：Ningbo University, 2017.
[18]赵品, 谢辅州, 孙振国. 材料科学基础教程[M]. 哈尔滨：哈尔滨工业大学出版社, 2002.
ZHAO Pin, XIE Fuzhou, SUN Zhenguo. Fundamentls of Materials Science[M]. Harbin: Harbin Institute of Technology Press, 2002.
[19]潘邻, 高万振, 潘春旭, 等. 碳化钨对钴基合金激光熔覆复合涂层组织、微区成分及硬度的影响[J]. 材料热处理学报, 2010,31(10):131-135.
PAN Lin, GAO Wanzhen, PAN Chunxu, et al. Influence of WC on Microstructure, Compositions of Micro-region and Microhardness of Laser Cladding Cobalt-based Alloy Layer[J]. Transactions of Materials and Heat Treatment, 2010, 31(10):131-135.