AA7075板材热处理的增塑机制及成形性能

doi:10.3969/j.issn.1004-132X.2020.17.016

摘要/Abstract

摘要： 结合生产工艺过程，研究了成形所需固溶处理、工序衔接所需自然时效、性能恢复所需人工时效对板材力学性能和成形性能的影响；通过金相显微镜、扫描电子显微镜和能谱分析等手段，探索热处理对板材显微组织与宏观力学性能的影响。结果表明：AA7075板材经固溶(480 ℃,0.5 h)水淬且自然时效处理后，最大力总伸长率提高85%、屈服强度降低60%，后经人工时效(120 ℃,12 h)处理，板材可完全恢复力学性能；固溶后,板材成形极限大幅提高，回弹比率显著减小；后继时效处理对弯曲角变化影响微弱。

关键词: AA7075铝合金, 热处理, 显微组织, 成形极限, 回弹

Abstract: Combined with production processes, effects of solution treatment required for forming, natural aging required for process connection, and artificial aging required for performance recovery on the mechanics properties and forming properties of the sheets were studied. The influences of heat treatment on the microstructure and macroscopic mechanics properties of the sheets were investigated by optical microscopy, scanning electron microscopy and energy dispersive spectroscopy. The results show that the percentage of total elongation at maximum force increases by 85% and yield strength decreases by 60% after the AA7075 sheets are heat-treated with solution treatment(480 ℃, 0.5 h) and natural aging. The sheets may restore mechanical properties completely after artificial aging(120 ℃, 12 h). The forming properties of the sheets are greatly improved and the rebound rate of the sheets is reduced significantly after solution treatment. The influence of subsequent aging treatment on the bending angle changes are weak.

Key words: AA7075 aluminum alloy, heat treatment, microstructure, forming limit, springback

中图分类号:

TG166.3

孙宇飞1;赵长财1;杨盛福2;杨卓云1. AA7075板材热处理的增塑机制及成形性能[J]. 中国机械工程, DOI: 10.3969/j.issn.1004-132X.2020.17.016.

SUN Yufei1;ZHAO Changcai1;YANG Shengfu2;YANG Zhuoyun1. Plasticizing Mechanism and Formability of AA7075 Sheet Heat Treatment[J]. China Mechanical Engineering, DOI: 10.3969/j.issn.1004-132X.2020.17.016.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: http://www.cmemo.org.cn/CN/10.3969/j.issn.1004-132X.2020.17.016

http://www.cmemo.org.cn/CN/Y2020/V31/I17/2128

参考文献

[1]刘辰辰, 陈亚军, 李柯, 等. 7075航空铝合金原位腐蚀-多轴疲劳行为分析[J].中国机械工程, 2019, 30(5): 615-621.
LIU Chenchen, CHEN Yajun, LI Ke, et al. Analysis for In-situ Corrosion-multiaxial Fatigue Behaviors of 7075 Aerospace Aluminum Alloys[J]. China Mechanical Engineering, 2019, 30(5): 615-621.
[2]PRABHURAJ P, RAJAKUMAR S, LAKSHMINARAYANAN A K, et al. Evaluating Stress Corrosion Cracking Behaviour of High Strength AA7075-T651 Aluminium Alloy[J]. Journal of the Mechanical Behavior of Materials, 2017, 26(3/4): 105-112.
[3]DONG Guojiang, ZHAO Changcai, PENG Yaxin, et al. Hot Granules Medium Pressure Forming Process of AA7075 Conical Parts[J]. Chinese Journal of Meghanical Engineering, 2015, 28(3): 580-591.
[4]LU Jue, SONG Yanli, HUA Lin, et al. Thermal Deformation Behavior and Processing Maps of 7075 Aluminum Alloy Sheet Based on Isothermal Uniaxial Tensile Tests[J]. Journal of Alloys and Compounds, 2018, 767: 856-869.
[5]DONG Guojiang, BI Jiang, DU Bing, et al. Research on AA6061 Tubular Components Prepared by Combined Technology of Heat Treatment and Internal High Pressure Forming[J]. Journal of Materials Processing Technology, 2017, 242: 126-138.
[6]MAHATHANINWONG N， PLOOKPHOL T， WANNASIN J, et al. T6 Heat Treatment of Rheocasting 7075 Al Alloy[J]. Materials Science & Engineering: A, 2012, 532: 91-99.
[7]GUO Fengbin, ZHU Baohong, JIN Longbing, et al. Microstructure and Mechanical Properties of 7A56 Aluminum Alloy after Solution Treatment[J]. Rare Metals, 2017, (7): 1-8.
[8]XU D K, ROMETSCH P A, BIRBILIS N. Improved Solution Treatment for an As-rolled Al-Zn-Mg-Cu Alloy. Part I. Characterisation of Constituent Particles and Overheating[J]. Materials Science & Engineering： A, 2012, 534: 234-243.
[9]SHAO Z, LI N, LIN J, et al. Development of a New Biaxial Testing System for Generating Forming Limit Diagrams for Sheet Metals under Hot Stamping Conditions[J]. Experimental Mechanics, 2016, 56(9): 1489-1500.
[10]王辉. 成形极限图的获取方法与其在金属板料成形中的应用[D]. 南京: 南京航空航天大学, 2011.
WANG Hui. Acquisition Method of Forming Limit Diagram and Its Application in Sheet Metal Forming[D].Nanjing： Nanjing University of Aeronautics and Astronautics, 2011.
[11]ZHANG R Y, ZHAO G Y, GUO Z H, et al. Effects of Material Parameters on Springback of 5052 Aluminium Alloy Sections with Hat Profile in Rotary Draw Bending[J]. The International Journal of Advanced Manufacturing Technology, 2015, 80(5/8): 1067-1075.
[12]GRZE R, MANACH P Y, LAURENT H, et al. Influence of the Temperature on Residual Stresses and Springback Effect in an Aluminium Alloy[J]. International Journal of Mechanical Sciences, 2010, 52(9): 1094-1100.
[13]LIU Zhiwen, LI Louxing, YI Jie, et al. Influence of Heat Treatment Conditions on Bending Characteristics of 6063 Aluminum Alloy Sheets[J]. Transactions of Nonferrous Metals Society of China, 2017, 27(7): 1498-1506.
[14]韩成府, 岑少起, 路王珂, 等. 固溶处理对7075铝合金组织和力学性能的影响[J]. 特种铸造及有色合金, 2017, 37(2): 201-204.
HAN Chengfu, CEN Shaoqi, LU Wangke, et al. Influence of Solution Treatment on Micorostructure and Mechanical Properties of 7075 Aluminum Alloy[J]. Special Casting & Nonferrous Alloys, 2017, 37(2): 201-204.
[15]ZOU Xiuliang, YAN Hong, CHEN Xiaohui. Evolution of Second Phases and Mechanical Properties of 7075 Al Alloy Processed by Solution Heat Treatment[J]. Transactions of Nonferrous Metals Society of China, 2017, 27(10): 2146-2155.
[16]HAN N M, ZHANG X M, LIU S D, et al. Effect of Solution Treatment on the Strength and Fracture Toughness of Aluminum Alloy 7050[J]. Journal of Alloys & Compounds, 2011, 509(10): 4138-4145.
[17]王路. 固溶过程中升温速率及淬火速率对7075铝合金板材的组织及性能的影响[D]. 重庆: 重庆大学, 2016.
WANG Lu. Effect of Heating Rate and Quenching Rate of Solution Treatment on Microstructure and Properties of 7075 Aluminum Alloy Sheets[D]. Chongqing: Chongqing University, 2016.
[18]LI Peiyue, XIONG Baiqing, ZHANG Yongan, et al. Temperature Variation and Solution Treatment of High Strength AA7050[J]. Transactions of the Nonferrous Metals Society of China, 2012, 22(3): 547-554.
[19]宗崇文. 7075铝合金时效成形力学性能及微观组织特征研究[D]. 南昌: 南昌航空大学, 2015.
ZONG Chongwen. Study on Mechanical Properties and Microstructure Characteristics of 7075 Aluminum Alloy after Age Forming[D]. Nanchang: Nanchang Hangkong University, 2015.
[20]LOU Yanshan, YOON Jeongwhan, HUH Hoon, et al. Correlation of the Maximum Shear Stress with Micro-mechanisms of Ductile Fracture for Metals with High Strength-to-weight Ratio[J]. International Journal of Mechanical Sciences, 2018，46/47:583-601.