薄壁扇形筋板挤压成形开裂抑制及翻转展宽策略

doi:10.3969/j.issn.1004-132X.2022.14.012

摘要/Abstract

摘要： 通过对大高厚比扇形筋板挤压成形机理进行数值模拟和物理实验，明确了扇形筋板局部变形不协调和角部应力集中是筋板角部产生开裂的主要原因。提出采用应力转移法在筋板成形初期提前预制局部切口，有效改变筋板内部拉应力分布形态，使筋板与侧壁的连接处拉应力由原有的120 MPa降低到50 MPa甚至更低。实验与模拟分析证明，预制切口可释放筋板自身变形约束，使筋板变形以切口为中心分界，左侧部分筋板向左侧面内弯曲，右侧部分筋板向右侧面内弯曲。得出在小拉应力作用下依靠筋板的面内弯曲可大幅度增加筋板长度的结论。

关键词: 精密挤压, 扇形筋板, 应力转移, 开裂, 数值模拟

Abstract: Through numerical simulation and physical experiments on extrusion forming mechanism of fan-shaped ribs with large ratio of height to thickness, it is found that the main causes of corner cracking are local deformation disharmony and corner stress concentration. A stress transfer method was proposed, where the local incision was prefabricated in advance at the initial stage of the rib forming, which might effectively change the distribution pattern of tensile stress inside the ribs and reduce the tensile stress at the connection between the rib and the side wall from 120 MPa to 50 MPa or even lower. Experimental and simulation analysis show that the precast incision may release the deformation constraint of the rib itself, the rib deformation with the incision as the central boundary, the left part of the ribs in the plane bending towards left side, the right part of the ribs in the plane bending towards the right side. It is concluded that the length of ribs may be greatly increased by in-plane bending under the action of small tensile stress.

Key words: precision extrusion, fan-shaped ribbing, stress-transfer, cracking, numerical simulation

中图分类号:

TG386

胡福泰, . 薄壁扇形筋板挤压成形开裂抑制及翻转展宽策略[J]. 中国机械工程, 2022, 33(14): 1734-1740.

HU Futai, . Cracking Suppression and Lateral Bending Broadening Strategy of Fan-shaped Thin-wall Ribs during Extrusion[J]. China Mechanical Engineering, 2022, 33(14): 1734-1740.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: http://www.cmemo.org.cn/CN/10.3969/j.issn.1004-132X.2022.14.012

http://www.cmemo.org.cn/CN/Y2022/V33/I14/1734

参考文献

［1］陈永来，张帆，单群，等.精密成形技术在航天领域的应用进展［J］.材料科学与工艺，2013，21（4）:57-64.
CHEN Yonglai, ZHANG Fan, SHAN Qun, et al. Application Progress of Precision Forming Technology in Aerospace［J］. Materials Science and Technology, 2013,21(4):57-64.
［2］PARK J J, HWANG H S. Preform Design for Precision Forging of an Asymmetric Rib-web Type Component［J］. Journal of Materials Processing Technology, 2007,187/188:595-599.
［3］李旭斌.高强铝合金复杂筋板构件整体成形技术研究［D］.太原：中北大学，2015.
LI Xubin. Study on Monolithic Forming Technology for Aldural Complex Rib-web Component［D］. Taiyuan：North University of China, 2015.
［4］孙志超，杨合，孙念光.钛合金整体隔框等温成形局部加载分区研究［J］.塑性工程学报,2009,16（1）：138-143.
SUN Zhichao, YANG He, SUN Nianguang. Simulation on Local Loading Partition during Titanium Bulkhead Isothermal Forming Process［J］. Journal of Plasticity Engineering, 2009, 16(1):138-143.
［5］张大伟，杨合. 钛合金筋板类构件局部加载成形中流向未加载区材料的分配［J］.稀有金属材料与工程，2014，43（2）:296-300.
ZHANG Dawei, YANG He. Distribution of Metal Flowing into Unloaded Area in the Local Loading Process of Titanium Alloy Rib-web Component［J］. Rare Metal Materials and Engineering, 2014, 43(2):296-300.
［6］张大伟.钛合金筋板类构件局部加载成形有限元仿真分析中的摩擦及其影响［J］.航空制造技术，2017(4):34-41.
ZHANG Dawei. Friction and Influence in FEM Simulation of Local Loading Process for Titanium Alloy Rib-web Component［J］. Aeronautical Manufacturing Technology, 2017 (4):34-41.
［7］刘伟，徐永超，陈一哲,等.薄壁曲面整体构件流体压力成形起皱机理与控制［J］.机械工程学报，2018，54（9）:37-44.
LIU Wei, XU Yongchao, CHEN Yizhe, et al. Mechanism and Controlling of Wrinkles during Hydroforming of Integral Thin-walled Curved Shell［J］. Journal of Mechanical Engineering, 2018, 54(9):37-44.
［8］梁柱，李国俊，张治民，等.5A06铝合金带筋薄板件挤压缺陷的模拟分析及优化［J］.锻压技术，2016，41（2）:51-57.
LIANG Zhu, LI Guojun, ZHANG Zhimin, et al. Simulation Analysis and Optimization of Extrusion Defects for Aluminum Alloy 5A06 Sheet with Rib［J］. Forging & Stamping Technology, 2016, 41(2):51-57.
［9］胡福泰，汪飞雪.复杂腔体直壁扇形筋板精密挤压成形缺陷控制［J］. 塑性工程学报，2021,28(3):1-6.
HU Futai, WANG Feixue. Defect Control of Precision Extrusion Forming of Complex Cavity Straight Fan-shaped Rib Plate［J］. Journal of Plasticity Engineering, 2021, 28(3):1-6.
［10］胡福泰，汪飞雪，张逸飞. 反挤压6063铝合金U形筋板面内应力分布及改善策略［J］. 塑性工程学报，2021,28(8):98-102.
HU Futai, WANG Feixue， ZHANG Yifei. Backward Extrusion Stress Distribution and Improvement Study of U-shaped Ribbing 6063 Aluminum Alloy［J］. Journal of Plasticity Engineering, 2021, 28(8):98-102.
［11］夏建芳，张明强，高放军.挤压参数及模具结构参数对某大长径比铝合金零件冷挤压流变成形载荷的影响［J］.现代制造工程, 2021 (10)：101-106.
XIA Jianfang, ZHANG Mingqiang, GAO Fangjun. Effect of Extrusion Parameters and Die Structure Parameters on Rheological Forming Load of a Large Aspect Ratio Aluminum Alloy Part during Cold Extrusion［J］. Modern Manufacturing Engineering, 2021 (10):101-106.
［12］李会知，杨建中，刘敏珊. 均布荷载作用下两端固支梁的弹塑性分析［J］. 河海大学学报（自然科学版）， 2005，33(4)：447-451.
LI Huizhi, YANG Jianzhong, LIU Minshan. Elastic-plastic Analysis of Beams Fixed at Two Ends Subjected to Uniformly-distributed Loads［J］. Journal of Hohai University (Natrure Science), 2005, 33(4)：447-451.
［13］樊友景，高建华，李大望. 均布荷载作用下两端固支梁的弹性力学解析解［J］. 河南科学，2006，24(2)：237-240.
FAN Youjing, GAO Jianhua, LI Dawang. Analytical Solution of the Elastic Mechanics for Static Indeterminate Beams Fixed at Two Sides under the Even Load［J］. Henan Science, 2006, 24(2)：237-240.
［14］杨庆平, 田宗漱.矩形凸肩板拉伸和弯曲时三维应力集中［J］.船舶力学，2004，8(5):62-70.
YANG Qingping, TIAN Zhongshu. Three-dimensional Stress Concentration in Shoulder Fillets under Tension and Bending［J］. Journal of Ship Mechanics, 2004, 8(5):62-70.

[1]	李燕乐, 潘忠涛, 戚小霞, 崔维强, 陈健, 李方义. 热处理工艺对激光熔覆316L温度场与应力场的影响规律[J]. 中国机械工程, 2024, 35(04): 666-677.
[2]	彭文飞, 张成, 林龙飞, 黄明辉, 余丰. 基于连续损伤力学的楔横轧芯部损伤建模及预测[J]. 中国机械工程, 2024, 35(04): 711-720,751.
[3]	李坤航, 张思琦, 吴玮, 胡明卓, 孙娅铃, 熊鑫, 黄宏. 三层异种不等厚钢电阻点焊多场耦合模拟与分析[J]. 中国机械工程, 2023, 34(24): 2996-3003.
[4]	骆文泽, 成慧梅, 刘红艳, 王义峰, 叶延洪, 邓德安. 高强钢Q960E对接接头残余应力与焊接变形的数值模拟[J]. 中国机械工程, 2023, 34(17): 2095-2105,2141.
[5]	朱玉龙, 赵迎松, 方阳, 陈洪恩, 陈振茂, . 孔边裂纹的旋转涡流检测[J]. 中国机械工程, 2023, 34(08): 883-891.
[6]	秦登, 戴志远, 周宁, 李田. 受电弓下沉对其气动和声学行为的影响[J]. 中国机械工程, 2022, 33(20): 2509-2519.
[7]	李伟, 郑颢, 刘彦梅, 范松. 汽车副车架安装螺栓碰撞断裂的数值模拟研究[J]. 中国机械工程, 2022, 33(19): 2388-2393.
[8]	马艺, 陈宇涛, 孟祥铠, 赵文静, 彭旭东, . 牙轮钻头用单金属密封瞬态启动动力学模型与密封性能[J]. 中国机械工程, 2022, 33(07): 777-785.
[9]	许明三, 周春辉, 张正, 曾寿金, . 激光熔覆过程中的粉、气、光耦合温度场[J]. 中国机械工程, 2022, 33(01): 70-77.
[10]	潘承怡, 童圆栖, 曹冠群, 赵彦玲. 微结构表面展开轮摩擦磨损特性与仿真研究[J]. 中国机械工程, 2021, 32(22): 2689-2696.
[11]	姜云禄, 杨亮, 韩晓辉, 徐野, 陈怀宁, 蔡桂喜. 运行条件对不锈钢点焊疲劳性能影响及开裂分析[J]. 中国机械工程, 2021, 32(14): 1726-1731.
[12]	朱谦, 游东东, 朱权利, . 基于摩擦模型的挤压铸造机压射机构动态配合[J]. 中国机械工程, 2021, 32(12): 1405-1413.
[13]	尹洪超, 刘宵, 翟镇德, 穆林. 多角度弯曲管磨粒流加工数值模拟研究[J]. 中国机械工程, 2021, 32(11): 1299-1306.
[14]	郭威, 孙洪鸣, 徐高飞, 李广伟, 周悦, 王敏健, . 全海深着陆车着底冲击特性与集中应力结构改进[J]. 中国机械工程, 2021, 32(07): 867-874.
[15]	杜飞;王新云;邓磊;夏巨谌;金俊松. 高速冲击连接技术的研究进展[J]. 中国机械工程, 2021, 32(05): 600-610.