镀锌量对低合金钢/5052铝合金感应静压焊接头微观组织与力学性能的影响

doi:10.3969/j.issn.1004-132X.2023.10.012

摘要/Abstract

摘要： 运用感应静压焊接技术制备了三种不同镀锌量低合金钢与铝合金的搭接接头，研究不同镀锌量对感应静压焊接头界面连接状态、微观组织形貌以及力学性能的影响规律。结果表明，三种不同镀锌量搭接接头连接界面较平直，连接质量良好。接头中间界面区由靠近钢侧的Fe2Al5和靠近铝侧的FeAl3组成。对比三种不同镀锌量接头微观组织发现，Zn元素能改善钢铝界面初始润湿机制，强化低合金钢与铝合金之间的连接效果，提高搭接接头力学性能。当使用镀锌量为140 g/m2的低合金钢板进行焊接时，在焊趾位置发现了明显的富锌区缺陷，导致接头剪切性能急剧下降。低合金钢板与铝合金的搭接接头的剪切性能随着镀锌量的增加呈现出先提高后降低的趋势，挑选厚度适中的镀锌层对提高接头力学性能具有重要意义。

关键词: 感应静压焊接, 镀锌量, 微观结构, 力学性能

Abstract: Three lap joints of low-alloy steel plates with different galvanizations and aluminum alloys were prepared using IPW technique. The effects of different amounts of galvanization on the interfacial connection state， microstructure characteristics and mechanics properties of the joints were studied. The results show that the connection interfaces of the three different amount of galvanization joints are straighter and the connection quality is good. The middle interface area of the joint consists of Fe2Al5 near the steel side and FeAl3 near the aluminum side. By comparing the microstructure and morphology of the joints with three different amount of galvanization， it is found that Zn element may improve the initial wetting mechanism at the steel-aluminum interfaces， strengthen the connection effect between aluminum alloy and low-alloy steel， and improve the mechanics properties of the lap joints. When welding with a low alloy steel plate with a galvanization of 140 g/m2， a significant zinc-rich zone defect is found at the weld toe position， resulting in a sharp drop in the shear properties of the joints. The shear properties of lap joints of low-alloy steel sheets and aluminum alloys show a trend of increasing and then decreasing with the amount of galvanization， and it is important to select a moderate thickness of galvanization to improve the mechanics properties of the joints.

Key words: , induction-pressure welding（IPW）, amount of galvanization, microstructure, mechanics property

中图分类号:

TG456.9

高恺, 李坤, 顾红历, . 镀锌量对低合金钢/5052铝合金感应静压焊接头微观组织与力学性能的影响[J]. 中国机械工程, 2023, 34(10): 1220-1229.

GAO Kai, LI Kun, GU Hongli, . Effects of Amount of Galvanization on Microstructure and Mechanics Properties of Joints Made by Induction-pressure Welding of Low Alloy Steel/5052 Aluminum Alloy[J]. China Mechanical Engineering, 2023, 34(10): 1220-1229.

导出引用管理器 EndNote|Ris|BibTeX

链接本文: http://www.cmemo.org.cn/CN/10.3969/j.issn.1004-132X.2023.10.012

http://www.cmemo.org.cn/CN/Y2023/V34/I10/1220

参考文献

［1］MILLER W S， ZHUANG L， BOTTEMA J， et al. Recent Development in Aluminium Alloys for the Automotive Industry［J］. Materials Science and Engineering：A， 2000， 280（1）：37-49.
［2］LIU W， MA J， ATABAKI M M， et al. Joining of Advanced High-strength Steel to AA 6061 Alloy by Using Fe/Al Structural Transition Joint［J］. Materials & Design， 2015， 68：146-157.
［3］CAO R， HUANG Q， CHEN J H， et al. Cold Metal Transfer Spot Plug Welding of AA6061-T6-to-galvanized Steel for Automotive Applications［J］. Journal of Alloys and Compounds， 2014， 585：622-632.
［4］SANTOS D， RAMINHOS H， COSTA M R， et al. Performance of Finish Coated Galvanized Steel Sheets for Automotive Bodies［J］. Progress in Organic Coatings， 2008， 62（3）：265-273.
［5］MA J， HAROONI M， CARLSON B， et al. Dissimilar Joining of Galvanized High-strength Steel to Aluminum Alloy in a Zero-gap Lap Joint Configuration by Two-pass Laser Welding［J］. Materials & Design， 2014， 58：390-401.
［6］WANG S， LUO K， SUN T， et al. Corrosion Behavior and Failure Mechanism of Electromagnetic Pulse Welded Joints between Galvanized Steel and Aluminum Alloy Sheets［J］. Journal of Manufacturing Processes， 2021， 64：937-947.
［7］MIRZA F A， MACWAN A， BHOLE S D， et al. Microstructure， Tensile and Fatigue Properties of Ultrasonic Spot Welded Aluminum to Galvanized High-strength-low-alloy and Low-carbon Steel sheets［J］. Materials Science and Engineering：A， 2017， 690：323-336.
［8］KOBAYASHI S， YAKOU T. Control of Intermetallic Compound Layers at Interface between Steel and Aluminum by Diffusion-treatment［J］. Materials Science and Engineering：A， 2002， 338（1/2）：44-53.
［9］van ALBOOM A， LEMMENS B， BREITBACH B， et al. Multi-method Identification and Characterization of the Intermetallic Surface Layers of Hot-dip Al-coated Steel：FeAl3 or Fe4Al13 and Fe2 Al5 or Fe2Al5+ x［J］. Surface and Coatings Technology， 2017， 324：419-428.
［10］KOUADRI-HENNI A. Effect of Welding Laser Process on Macrostructures and the Mechanical prop Erties of Coating Steel DP600：Influence of Vaporization Zinc［J］. Journal of Manufacturing Processes， 2017， 30：83-96.
［11］谷晓燕，刘亚俊，孙大千，等. S355 钢/6005A 铝合金瞬间液相扩散连接接头组织与性能［J］. 吉林大学学报：工学版， 2017， 47（5）：1534-1541.
GU Xiaoyan， LIU Yajun， SUN Daqian et al. Microstructures and Mechanical Properties of Transient Liquid Phase Diffusion Bonded S355 Steel/6005A Alloy Joint［J］. Journal of Jilin University（Engineering and Technology Edition）， 2017， 47（5）：1534-1541.
［12］JINDAL V， SRIVASTAVA V C. Growth of Intermetallic Layer at Roll Bonded IF-steel/Aluminum Interface［J］. Journal of Materials Processing Technology， 2008， 195（1/3）：88-93.
［13］TAKATA N， NISHIMOTO M， KOBAYASHI S， et al. Crystallography of Fe2Al5Phase at the Interface between Solid Fe and Liquid Al［J］. Intermetallics， 2015， 67：1-11.
［14］蒋淑英，李世春. Al-Fe 液/固复合界面扩散溶解层研究［J］. 材料工程， 2009（增刊2）：236-240.
JIANG Shuying， LI Shichun. Diffusion Solution Zone of Al-Fe Liquid/Solid Interface［J］. Journal of Materials Engineering， 2009（S2）：236-240.
［15］JIANG W， FAN Z， LI G， et al. Effects of Zinc Coating on Interfacial Microstructures and Mechanical Properties of Aluminum/Steel Bimetallic Composites［J］. Journal of Alloys and Compounds， 2016， 678：249-257.
［16］FENG J， XUE S. Growth Behaviors of Intermetallic Compound Layers in Cu/Al Joints Brazed with Zn-22Al and Zn-22Al-0. 05 Ce Filler Metals［J］. Materials & Design， 2013， 51：907-915.
［17］GATZEN M， RADEL T， THOMY C， et al. The Role of Zinc Layer during Wetting of Aluminiumon Zinc-coated Steel in Laser Brazing and Welding［J］. Physics Procedia， 2014， 56：730-739.
［18］LIN J， LEI Y， LU L， et al. Effect of Temperature and Zinc Coating on Interfacial Bonding between Steel and Aluminum Dissimilar Material［J］. Procedia Manufacturing， 2019， 37：273-278.
［19］JIA L， SHICHUN J， YAN S， et al. Effects of Zinc on the Laser Welding of an Aluminum Alloy and Galvanized Steel［J］. Journal of Materials ProcessingTechnology， 2015， 224：49-59.
［20］赵磊，孙勇，李玉阁，等. 微合金化元素对 Fe-Al 界面结合的第一性原理研究［J］. 原子与分子物理学报， 2007， 24（4）：853-857.
ZHAO Lei， SUN Yong， LI Yuge， et al. First-principles Studies of the Effects of Microalloy Elements on Fe/Al Interface［J］. Journal of Atomic and Molecular Physics， 2007， 24（4）：853-857.
［21］NAKANO J， MALAKHOV D V， YAMAGUCHI S， et al. A Full Thermodynamic Optimization of the Zn-Fe-Al System within the 420～500 ℃ Temperature Range［J］. Calphad， 2007， 31（1）：125-140.
［22］SUNDMAN B， OHNUMA I， DUPIN N， et al. An Assessment of the Entire Al-Fe System Including D03 Ordering［J］. Acta Materialia， 2009， 57（10）：2896-2908.
［23］黄健康，刘宁，何翠翠，等. 铝／镀锌钢焊接接头金属间化合物热力学分析［J］. 哈尔滨工程大学学报， 2016， 37（6）：837-841.
HUANG Jiankang， LIU Ning， HE Cuicui， et al. Thermodynamics Analysis of Intermetallic Compounds on Aluminum-steel Welded Joint［J］. Journal of Harbin Engineering University， 2016， 37（6）：837-841.
［24］SUN H， YU G， CHEN S， et al. Effect of ZnAlFiller Metals on the Characteristics of the Joint Made by the High-frequency Induction Brazing of 304 Stainless Steel and 6A02 Aluminum［J］. Journal of Manufacturing Processes， 2021， 68：961-972.
［25］KOUADRI-HENNI A. Effect of Welding Laser Process on Macrostructures and the Mechanical Properties of Coating Steel DP600：Influence of Vaporization Zinc［J］. Journal of Manufacturing Processes， 2017， 30：83-96.
［26］HAO Y， CHEN N， WANG H P， et al. Effect of Zinc Vapor Forces on Spattering in Partial Penetration Laser Welding of Zinc-coated Steels［J］. Journal of Materials Processing Technology， 2021， 298：117282.
［27］JIN X， BI W， WANG L， et al. Root Cause Analysis of Pinhole Defects on Painted Galvanized Steel Panel［J］. Engineering Failure Analysis， 2020， 115：104598.
［28］吴程浩，刘涛，高嵩，等. 铝/钢异种金属的超声振动强化搅拌摩擦焊接工艺［J］. 材料工程， 2022， 50（1）：33-42.
WU Chenghao， LIU Tao， GAO Song， et al. Ultrasonic Vibration Enhanced Friction Stir Welding Process of Aluminum/Steel Dissimilar Metals［J］. Journal of Materials Engineering， 2022， 50（1）：33-42.
［29］卢源志，刘金水，周惦武，等. 双相钢/铝合金激光搭接焊添加Mn粉的作用［J］. 中国有色金属学报， 2016（8）：1632-1640.
LU Yuanzhi， LIU Jinshui， ZHOU Dianwu， et al. Laser Lap Welding Joints in Dual Phase Steel/Aluminum Alloy with Mn Powder Addition［J］. The Chinese Journal of Nonferrous Metals， 2016（8）：1632-1640.

[1]	倪敬, 崔智, 何利华, 付新, 朱泽飞. 聚四氟乙烯材料切削工艺和应用研究进展[J]. 中国机械工程, 2024, 35(03): 498-514.
[2]	王伟, 马乾伦, 白振华, 王子昂. 基于梯度提升决策树的冷轧高强钢卷力学性能预测[J]. 中国机械工程, 2023, 34(18): 2222-2229.
[3]	刘莹, 陈越, 赵雪利, 于同敏, 祝铁丽, . 超声辅助注射成形碳纤维增强聚丙烯制件性能研究[J]. 中国机械工程, 2023, 34(16): 1975-1981.
[4]	李光俊, 段宏, 徐磊, 阚琛, 刘忠亮, 高晓东. Al7.8Co20.6Cr12.2Fe11.5Ni40.7Ti7.2高熵超合金的摩擦磨损行为研究[J]. 中国机械工程, 2023, 34(13): 1568-1575.
[5]	周后明, 陈皓月, 李神贵. 基于梯度结构的Al2O3/ZrO2陶瓷刀具材料的制备及其力学性能[J]. 中国机械工程, 2023, 34(10): 1199-1207.
[6]	杨硕, 张杰, 孔宁, 王浩威, 王晓宇, 庄原. 航天用大展收比豆荚结构变形规律模型及其仿真验证[J]. 中国机械工程, 2023, 34(07): 780-788.
[7]	张岩, 黄传真, 刘含莲. 氮化碳基陶瓷刀具材料的制备与力学性能研究[J]. 中国机械工程, 2023, 34(03): 352-358，368.
[8]	方学伟, 蒋笑, 王喆, 武晓康, 黄科. ER120S-G高强钢电弧增材制造的工艺优化[J]. 中国机械工程, 2023, 34(02): 218-225.
[9]	蒋创宇, 张保强, 陈云, 王存福, 罗华耿, 胡杰翔, 曹龙超. Gyroid结构力学性能及数值收敛性研究[J]. 中国机械工程, 2022, 33(23): 2790-28000.
[10]	焦晨, 晁龙, 朱磊, 沈理达, 梁绘昕, 戴宁, 王长江, 孙骏. 面向骨科植入物的仿生多孔结构设计与制造方法[J]. 中国机械工程, 2022, 33(23): 2844-2850.
[11]	汤永锋, 路平, 刘斌, 江开勇, 颜丙功, 刘嘉伟, 韩伟, . 不同梯度变化方式的不规则多孔结构设计与力学性能分析[J]. 中国机械工程, 2022, 33(23): 2859-2866.
[12]	张帅, 陈照强, 肖光春, 衣明东, 张静婕, 周婷婷, 许崇海. Si3N4/TiC/ZrSi2陶瓷刀具裂纹愈合性能研究[J]. 中国机械工程, 2022, 33(19): 2288-2297.
[13]	曾寿金, , 李传生, 刘广, 许明三, 李涤尘. 选区激光熔化梯度多孔支架力学性能和能量吸收研究[J]. 中国机械工程, 2022, 33(19): 2364-2371.
[14]	仲杨, 秦晓波, 郑志镇, 李建军, 王承. 石化容器用2.25Cr-1Mo-0.25V钢的CMT电弧熔丝增材制造工艺及组织性能研究[J]. 中国机械工程, 2022, 33(10): 1251-1259.
[15]	郑宇, 郭策, 马耀鹏, 管吉钢. 仿生多层级柔性轻质结构的设计、制备及力学性能分析[J]. 中国机械工程, 2021, 32(23): 2876-2882.