Study on Fabrication of Superhydrophobic Surface Substrate Based on ECM

China Mechanical Engineering ›› 2011, Vol. 22 ›› Issue (19): 2354-2359.

Previous Articles Next Articles

Study on Fabrication of Superhydrophobic Surface Substrate Based on ECM

Xu Wenji1;Dou Qingle1;Sun Jing1;Song Jinlong1;Pang Guibing2

1.Dalian University of Technology,Dalian,Liaoning,116024

2.Dalian Polytechnic University,Dalian,Liaoning,116034

Online:2011-10-10 Published:2011-10-12
Supported by:

Major Research Program of National Natural Science Foundation of China（No. 90923022）
National Natural Science Foundation of China（No. 50905020）

基于电化学加工方法的铝基超疏水表面制备技术研究

徐文骥1;窦庆乐1;孙晶1;宋金龙1;庞桂兵2

1.大连理工大学,大连,116024

2.大连工业大学,大连,116034

基金资助:
国家自然科学基金重大研究计划资助项目(90923022)；国家自然科学基金资助项目(50905020)
Major Research Program of National Natural Science Foundation of China（No. 90923022）
National Natural Science Foundation of China（No. 50905020）

Abstract

Abstract:

A new method of fabrication superhydrophobic surface by means of ECM was developed. The fabrication mechanism was based on the fact that the grain boundaries/dislocations were micro/nano-scale and more likely to be anodic dissolved than that of grain self, so the multi-scale micro/nano-structures surface can be generated by an applied electric field and the chemical solution. The relationship among processing quality, efficiency and conditions was studied in experiments herein.The results show that ECM can be used to fabricate dual-scale micro/nano-structures on aluminum surfaces, and further applied to generate the large size of superhydrophobic surface. The method is easier to control the reaction process than chemical etching meanwhile more economical than other techniques. After modified with low surface energy materials, the surface exhibits superhydrophobic property with water contact angle of 167° and tilt angle less than 3°.

Key words: electrochemical machining(ECM), superhydrophobic surface, micro/nano-structure, grain boundary, dislocation

摘要：

鉴于金属铝表面存在微米级的晶界和纳米级的位错,在外加电场和电解液的作用下,晶界位错处因具有更高的位能会使得阳极优先溶解,进而形成微纳米结构相结合的粗糙表面,提出一种新的铝基超疏水表面的电化学制备方法,实验研究了其加工质量、加工效率和加工条件之间的关系,结果显示电化学加工方法能够在铝基底上制备出多阶层微/纳米结构,可用作超疏水表面基底。电化学加工比化学刻蚀法有更好的可控性,同时比光刻等方法更经济。所加工表面经过低表面能材料修饰后呈现超疏水的特性,与水滴的接触角达到167°,滚动角小于3°。

关键词:

电化学加工, 超疏水表面, 微/纳米结构, 晶界, 位错

CLC Number:

TG66

XU Wen-Ji-1, DOU Qiang-Le-1, SUN Jing-1, SONG Jin-Long-1, LONG Gui-Bing-2.

Study on Fabrication of Superhydrophobic Surface Substrate Based on ECM

[J]. China Mechanical Engineering, 2011, 22(19): 2354-2359.

徐文骥1, 窦庆乐1, 孙晶1, 宋金龙1, 庞桂兵2.

基于电化学加工方法的铝基超疏水表面制备技术研究

[J]. 中国机械工程, 2011, 22(19): 2354-2359.

References

[1]Liu T, Lau K T,Chen S G,et al. Super hydrophobic Surfaces Improve Corrosion Resistance of Fe2 Al-type Intermetallie in Seawater[J]. Advanced Materials Re- search,2008,47/50( 1 ) : 73-176.
[2]Shi F, Niu J, Liu J L, et al. Towards Understanding Why a Superhydrophobic Coating is Needed by Water Striders[J]. Advanced Materials, 2007, 19 ( 17 ) : 2257-2261.
[3]McHale G, Shirtcliffe N J, Evans C R, et al. Terminal Velocity and Drag Reduction Measurements on Super hydrophobic Spheres [J].Applied Physics l.euers, 2009,94(6) :064104.
[4]袁志庆[1,2],陈洪[1,2],汤建新[3],石璞[3],张继德[3],赵德坚[3],曾艳清[4],龚慧芳[3],付欣[3].超疏水聚丙烯表面的制备及血液相容性研究[J].功能材料:1359-1362.
[5]Tsujii K, Yamamoto T, Onda T, et al. Super Oil - re pellem Surfaces[J]. Angew. Chem. Int. Ed. Engl. 1997, 36(9):1011-1012.
[6]Shibuichi S, Yamarnoto T, Onda T, et al. Super Water --and Oil- repellent Surfaces Resulting from Fractal Structure[J]. Journal of Colloid and Interface Science, 1998,208(1) :194-287.
[7]Wu W C, Wang X L, Wang D A, et al. Alumina Nanowire Forests Via Unconventional Anodization and Super--repellency Plus Low Adhesion to Diverse Liquids[J]. Chem. Commun. 2009,9 (2) : 1043-1045.
[8]Wang H, Dai D, Wu X D. Fabrication of Superhydro phobic Surfaces on Aluminum[J]. Applied Surface Sci ence, 2008,254 ( 17 ) : 5599-5601.
[9]Qian B T, Shen Z Q. Fabrication of Superhydrophobic Surfaces by Dislocation--selective Chemical Etching on Aluminum,Copper, and Zinc Substrates [J]. Langmuir 2005,21 (20) : 9007-9009.
[10]Sarkar D K, Farzaneh M, Paynter R W. Superhydro phobic Properties of Ultrathin Rf -sputtered Teflon Films Coated Etched Aluminum Surfaces[ J]. Materi als Leters 2008,62(8/9) : 1226-1229.
[11]Guo Z G,Zhou F, Hao J C, et al. Effects of System Parameters on Making Aluminum Alloy Lotus[J].Journal of Colloid and Interface Science, 2006, 303(1) :298-305.
[12]Gross M,VarniK F, Raabe D, et al. Small Droplets on Superhydrophobic Substrates [J]. Physical Review, 2010,81(5) :05606-1-05606-14.
[13]Good R J,Girifalco L A. A Theory Surface and Imerfacial Hnergies. Ⅲ. ergies of Solids from Journal of Physical Ch for Fstimation of Energies of Solids from Contact Angle Data[J]. The Journal of Physical Chemistry, 1960,64 ( 5 ) :561-565.
[14]朱定一[1],戴品强[1],罗晓斌[1],张远超[1].润湿性表征体系及液固界面张力计算的新方法（Ⅱ）[J].科学技术与工程,2007,7(13):3063-3069.
[15]Wenzel R N. Resistence of Solid Surfaces to Wetting by Water[J]. Industrial and Engineering Chemistry, 1936,28 (8) : 988-994.
[16]Henderson B.晶体缺陷[M].范印哲,译.北京:高等教育出版社,1983.
[17]Cassie A B,Baxter S. Wettability of Porous Surfaces [J]. Transaction of Faraday Socciety, 1944, 40 : 546-551.
[18]徐家文,云乃彰,王建业,等.电化学加工技术[M].北京:国防工业出版社,2008.
[19]Hull D,Bacon DJ.位错导论[M].丁树深,李齐,泽.北京:科学出版社,1990.
[20]Schondelmaier D, Cramm S,Klingeler R, et al. Orien- tation and Self--assembly of Hydrophobie Fluoroalkyl -- silanes[J]. Langmuir,2002,18(16):6242-6245.

Study on Fabrication of Superhydrophobic Surface Substrate Based on ECM

基于电化学加工方法的铝基超疏水表面制备技术研究

PDF

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 4

Recommended Articles

Metrics

[1]	HUANG Yun, HUANG Jianchao, XIAO Guijian, LIU Shuai, LIN Ouchuan, LIU Zhenyang. Research Progresses of Superhydrophobic Surface Processing Technology and Abrasion Resistance [J]. China Mechanical Engineering, 2024, 35(01): 2-26.
[2]	WANG Quanlong1;ZHANG Chaofeng1;WU Meiping1，2;CHEN Jiaxuan3. Subsurface Damage Mechanism of Nano Polycrystalline Coppers in Single Point Diamond Turning [J]. China Mechanical Engineering, 2019, 30(23): 2790-2797,2808.
[3]	ZHANG Hua-1, XU Jia-Wen-2, DIAO Jian-She-2. Simulation and Experimental Research on Jet Electrolytic Drilling [J]. China Mechanical Engineering, 2011, 22(21): 2624-2627.
[4]	LI Jian-Zhong, CHEN Fei-Hu, YAN Guo-Jiang, TU Jie-Yuan. Study on Influences of Grain Boundary and Grain on Machining Performance of Micro-EDM [J]. China Mechanical Engineering, 2011, 22(13): 1601-1604.