Numerical Simulation on Influences of Impact Angles of Blunt-nosed Projectile on Failure Characteristics for 2A12-T4 Aluminum Alloy Plates

Abstract

Abstract: A simulation model was established using finite element software ABAQUS， and the numerical simulations of 38CrSi steel projectile impacting 2A12-T4 aluminum alloy plates were conducted， then the influences of impact angles of projectile on the failure characteristics of target and ballistic attitude of projectile were analyzed.Based on numerical simulation and experimental results， the failure characteristics of the target were analyzed， the change laws of the dominant failure modes under different impact conditions， as well as the influences on the impact resistance of target because of that were established.The results show that with the increases of impact angles the ballistic limit velocity decreases， and then increases， and the ballistic limit reaches the minimum when the impact angle is about 15 degrees.In addition， the impact angle of projectile impacting greatly influences the failure mode of target， with the projectile angle increases， the dominant failure mode of target changes from shearing to tearing， and also increasing the degree of tearing the target.The initial impact angle and velocity of projectile have great influences on the trajectory attitude of the projectile during the impacts， especially in the vicinity of the ballistic limit velocity.

Key words: impact, 2A12-T4 aluminum alloy plate, blunt-nosed projectile, failure model

摘要： 利用有限元软件ABAQUS建立模拟模型，开展38CrSi钢弹体撞击2A12-T4铝合金板数值模拟研究，分析撞击过程中弹体撞击角度对弹道姿态及靶体失效特性的影响。基于数值仿真和实验结果，分析靶体的失效特性，确立不同撞击条件下靶体主要失效模式的转变规律，以及由此对靶体抗撞击性能的影响。研究结果表明：弹体的弹道极限速度随其撞击角度的增大先减小后增大，弹道极限速度在撞击角度约为15°时达到最小值；弹体撞击角度对靶体失效模式存在很大影响，随着弹体撞击角度的增大，靶体主要失效模式由剪切破坏逐渐过渡到撕裂破坏，靶体的撕裂程度不断加剧；弹体初始撞击角度和速度对其在撞击过程中的弹道姿态存在影响，在弹道极限速度附近表现尤为显著。

关键词: 撞击, 2A12-T4铝合金板, 平头弹体, 失效模式

CLC Number:

O385
O347

HU Jing;DENG Yunfei;CUI Yanan;ZHANG Yinbo. Numerical Simulation on Influences of Impact Angles of Blunt-nosed Projectile on Failure Characteristics for 2A12-T4 Aluminum Alloy Plates[J]. China Mechanical Engineering.

胡静;邓云飞;崔亚男;张银波. 平头弹撞击角度对2A12-T4铝合金板失效特性影响的数值模拟[J]. 中国机械工程.

References

[1]GUPTA P K，IQBAL M A，MOHAMMAD Z.Energy Dissipation in Plastic Deformation of Thin Aluminum Targets Subjected to Projectile Impact[J].International Journal of Impact Engineering，2017，110：85-96.
[2]MOHAMMAD Z，GUPTA P K，IQBAL M A，et al.Absorption in Metallic Targets Subjected to Oblique Impact[J].Procedia Engineering，2017，173：145-152.
[3]IQBAL M A，SENTHIL K，MADHU V，et al.Oblique Impact on Single， Layered and Spaced Mild Steel Targets by 7.62 AP Projectiles[J].International Journal of Impact Engineering，2017，110：26-38.
[4]FORRESTAL M J，B?RVIK T，WARREN T L，et al.Perforation of 6082-T651 Aluminum Plates with 7.62 mm APM2 Bullets at Normal and Oblique Impacts[J].Experimental Mechanics，2014，54：471-481.
[5]GUPTA N K，MADHU V.An Experimental Study of Normal and Oblique Impact of Hard-core Projectile on Single and Layered Plates[J].International Journal of Impact Engineering，1997，19（5）：395-414.
[6]王国荣，钱权，楚飞，等.高压流体入射角对节流阀材料的冲蚀预测及验证[J].中国机械工程，2017， 28（14）：1652-1657.
WANG Guorong，QIAN Quan，CHU Fei，et al.Erosion Prediction and Verification for Throttle Vale Materials about Incident Angles at High Pressure Fluids[J]. China Mechanical Engineering，2017，28（14）：1652-1657.
[7]魏刚.金属动能弹变形与断裂特性及其机理研究[D].哈尔滨：哈尔滨工业大学，2014.
WEI Gang.Investigation of Deformation and Fracture Behavior Associated Mechanisms of the Metal Kinetic Energy Projectiles[D].Harbin：Harbin Institute of Technology，2014.
[8]JOHNSON G R，COOK W H.A Constitutive Model and Data for Metals Subjected to Large Strains， High Strain Rates and High Temperatures[C]//Proceedings of the Seventh International Symposium on Ballistics.Hague，Netherlands，1983：541-547.
[9]JOHNSON G R，COOK W H.Fracture Characteristics of Three Metals Subjected to Various Strains， Strain Rates，Temperatures and Pressures[J].Engineering Fracture Mechanics，1985，21：31-48.
[10]张伟，魏刚，肖新科.2A12铝合金本构关系和失效模型[J].兵工学报，2013，34（3）：276-282.
ZHANG Wei，WEI Gang，XIAO Xinke.Constitutive Relation and Fracture Criterion of 2A12 Aluminum Alloy[J].Acta Armamentarii，2013，34（3）：276-282.

[1]	CHEN Lian, WEI Xiaohu, CAO Qiang, ZHOU Yan, YANG Yingxin, HU Chuan, ZHAO Zhijie, WU Bin. Mechanism of Rock Breaking by Convex Non-planar PDC Cutter and Its Applications in Gravel-bearing Formation [J]. China Mechanical Engineering, 2024, 35(02): 371-379.
[2]	WU Zhifeng, GAO Jianxiong, XU Rongxia, ZHU Pengnian. A Non-uniform Damage Accumulation Model Considering Load Interactions [J]. China Mechanical Engineering, 2023, 34(22): 2659-2664，2673.
[3]	ZHA Xuming, YUAN Zhi, QIN Hao, XI Linqing, ZHANG Tao, JIANG Feng. Ultrasonic Impact Strengthening of Titanium Alloys：State-of-the-art and Prospectives [J]. China Mechanical Engineering, 2023, 34(19): 2269-2287.
[4]	ZHOU Guoqiang, WANG Hui, SONG Yuning, ZHAO Guochao, . Design of Double-stage Safety Valves for Hydraulic Support and Experimental Study of Their Rapid Dynamic Load Impact Test [J]. China Mechanical Engineering, 2023, 34(18): 2194-2203.
[5]	WANG Liangwen, KONG Yangguang, WANG Ruolan, ZHANG Zhigang, LIU Xuling, LI Linfeng, . Simulation and Experimental Study of Contact-collision of Inner Braced Manipulators for Grasping Thin-walled Fragile Cylindrical Inner Wall Workpieces [J]. China Mechanical Engineering, 2023, 34(17): 2026-2036.
[6]	WU Hequan, BIAN Chuhong, HU Lin, GONG Chuangye. Research on Injury of Occupants with Different Postures in Rear End Impacts during Automatic Driving [J]. China Mechanical Engineering, 2023, 34(13): 1628-1637.
[7]	GU Zhenyu, HE Yi, LI Dongyang. Assessment Method of Environmental Impact of Casting Processes Based on Digital Twin [J]. China Mechanical Engineering, 2023, 34(12): 1465-1475.
[8]	XU Long, HU Zhiqiang, YANG Yi, WANG Chao, . Study on Engagement Characteristics of Gear Overrunning Clutch of Aquatic-aerial Amphibious Propellers [J]. China Mechanical Engineering, 2023, 34(09): 1126-1133.
[9]	SHEN Minmin, SUN Chuanbin, TONG Baohong, HOU Tongshen. Effects of Porous Baffle on Characteristics of Liquid Sloshing Impact Pressure [J]. China Mechanical Engineering, 2022, 33(24): 2953-2960.
[10]	CONG Jianchen, NI Peixiang, SUN Jun, LYU Shijie. Experimental Research and Analysis on Torsional Fatigue Strength of Engine Crankshafts [J]. China Mechanical Engineering, 2022, 33(18): 2197-2204.
[11]	YANG Jingjing, LI Cheng, TIE Ying. Low-velocity-impact Resistance Property of Sandwich Plates with Aluminum Folded Core [J]. China Mechanical Engineering, 2022, 33(13): 1629-1637.
[12]	BAI Shuwei, JIANG Nan, TONG Mingbo, CHANG Wenkui. Random Failure Model and Multi-element Damage Assessment of Long Endurance Aircrafts [J]. China Mechanical Engineering, 2021, 32(22): 2667-2672.
[13]	LI Yunfeng, SHI Yan, . Influences of Pulse Frequency on Microstructure and Properties in Laser Cladding Layers [J]. China Mechanical Engineering, 2021, 32(17): 2108-2117,2124.
[14]	ZHAO Qiaoli, HOU Yuliang, LIU Zeyi, LI Cheng. Multi-scale Analysis of LVI and CAI Behaviors of Plain Woven Carbon-fiber-reinforced Composites [J]. China Mechanical Engineering, 2021, 32(14): 1732-1742.
[15]	XU Zhangjing, LIU Zhiping, DU Yong, WU Hao. Design of Ultrasonic Weak Impact Energy Guide Device and Infrared Thermal Image Detection#br# [J]. China Mechanical Engineering, 2021, 32(12): 1387-1394.